Para-aramid threads
| Linear density | Filaments (f) | Tensile strength | Breaking force | Relative elongation at break | ||||
|---|---|---|---|---|---|---|---|---|
| denier | dtex | ea | g/d | Mpa | cN/tex | kgf | N | % |
| 130 | 143 | 90 | 22.6 | 2880 | 200 | 2.9 | 29 | 2.8 |
| 200 | 220 | 133 | 22.6 | 2880 | 200 | 4.5 | 44 | 2.9 |
| 300 | 330 | 200 | 22.6 | 2880 | 200 | 6.7 | 66 | 3.2 |
| 400 | 440 | 267 | 22.6 | 2880 | 200 | 9.0 | 88 | 3.2 |
| 600 | 660 | 400 | 22.6 | 2880 | 200 | 13.5 | 132 | 3.2 |
| 800 | 880 | 536 | 26.6 | 3384 | 235 | 21.3 | 209 | 3.5 |
| 840 | 930 | 560 | 26.6 | 3384 | 235 | 22.5 | 221 | 3.5 |
| 1000 | 1100 | 665 | 26.0 | 3312 | 230 | 26.3 | 258 | 3.6 |
| 1500 | 1670 | 1000 | 26.0 | 3312 | 230 | 39.4 | 386 | 3.6 |
| 3000 | 3300 | 2000 | 25.4 | 3240 | 225 | 77.1 | 756 | 3.8 |